Two major uses of GGBS are in the production of quality-improved slag cement, namely Portland Blastfurnace cement (PBFC) and High Slag Blastfurnace cement (HSBFC), with GGBS content ranging typically from 30 to 70%; and in the production of ready-mixed or site-batched durable concrete.
Concrete made with GGBS cement sets more slowly than concrete made with ordinary Portland cement, depending on the amount of GGBS in the cementitious material, but also continues to gain strength over a longer period in production conditions. This results in lower heat of hydration and lower temperature rises, and makes avoiding cold joints easier, but may also affect construction schedules where quick setting is required.
Use of GGBS significantly reduces the risk of damages caused by alkali-silica reaction (ASR), provides higher resistance to chloride ingress — reducing the risk of reinforcement corrosion — and provides higher resistance to attacks by sulfate and other chemicals.
The use of GGBS cement in concrete in Ireland is covered in the new Irish concrete standard IS EN 206-1:2002. This standard establishes two categories of additions to concrete along with ordinary Portland cement: nearly inert additions (Type I) and pozzolanic or latent hydraulic additions (Type II). GGBS cement falls in to the latter category. As GGBS cement is slightly less expensive than Portland cement, concrete made with GGBS cement will be similarly priced to that made with ordinary Portland cement.
To protect against chloride attack, GGBS is used at a replacement level of 50% in concrete. Instances of chloride attack occur in reinforced concrete in marine environments and in road bridges where the concrete is exposed to splashing from road de-icing salts. In most NRA projects in Ireland GGBS is now specified in structural concrete for bridge piers and abutments for protection against chloride attack. The use of GGBS in such instances will increase the life of the structure by up to 50% had only Portland cement been used, and precludes the need for more expensive stainless steel reinforcing.
GGBS is also routinely used to limit the temperature rise in large concrete pours. The more gradual hydration of GGBS cement generates both lower peak and less total overall heat than Portland cement. This reduces thermal gradients in the concrete, which prevents the occurrence of microcracking which can weaken the concrete and reduce its durability, and was used for this purpose in the construction of the Jack Lynch Tunnel in Cork.
Two major uses of GGBS are in the production of quality-improved slag cement, namely Portland Blastfurnace cement (PBFC) and High Slag Blastfurnace cement (HSBFC), with GGBS content ranging typically from 30 to 70%; and in the production of ready-mixed or site-batched durable concrete.
Concrete made with GGBS cement sets more slowly than concrete made with ordinary Portland cement, depending on the amount of GGBS in the cementitious material, but also continues to gain strength over a longer period in production conditions. This results in lower heat of hydration and lower temperature rises, and makes avoiding cold joints easier, but may also affect construction schedules where quick setting is required.
Use of GGBS significantly reduces the risk of damages caused by alkali-silica reaction (ASR), provides higher resistance to chloride ingress — reducing the risk of reinforcement corrosion — and provides higher resistance to attacks by sulfate and other chemicals.
The use of GGBS cement in concrete in Ireland is covered in the new Irish concrete standard IS EN 206-1:2002. This standard establishes two categories of additions to concrete along with ordinary Portland cement: nearly inert additions (Type I) and pozzolanic or latent hydraulic additions (Type II). GGBS cement falls in to the latter category. As GGBS cement is slightly less expensive than Portland cement, concrete made with GGBS cement will be similarly priced to that made with ordinary Portland cement.
To protect against chloride attack, GGBS is used at a replacement level of 50% in concrete. Instances of chloride attack occur in reinforced concrete in marine environments and in road bridges where the concrete is exposed to splashing from road de-icing salts. In most NRA projects in Ireland GGBS is now specified in structural concrete for bridge piers and abutments for protection against chloride attack. The use of GGBS in such instances will increase the life of the structure by up to 50% had only Portland cement been used, and precludes the need for more expensive stainless steel reinforcing.
GGBS is also routinely used to limit the temperature rise in large concrete pours. The more gradual hydration of GGBS cement generates both lower peak and less total overall heat than Portland cement. This reduces thermal gradients in the concrete, which prevents the occurrence of microcracking which can weaken the concrete and reduce its durability, and was used for this purpose in the construction of the Jack Lynch Tunnel in Cork.
|
|
|
|
|
|
|
|
|
|
|
|