The earliest commercial synthetic resin is based on a Phenol formaldehyde resin (PF) with the commercial name Bakelite, and is formed from an elimination reaction of phenol with formaldehyde. Phenol is reactive towards formaldehyde at the ortho and para sites (sites 2, 4 and 6) allowing up to 3 units of formaldehyde to attach to the ring. This forms a hydroxymethyl phenol. The hydroxymethyl group is capable of reacting with either another free ortho or para site, or with another hydroxymethyl group. The first reaction forms a methylene bridge, and the second forms an ether bridge.
Phenol formaldehyde resins, as a group, are formed by a step-growth polymerization reaction which may be either acid or base catalysed. The pathway the reaction follows varies depending on the catalyst type used.
Acid catalysed phenol formaldehyde resins are made with a molar ratio of formaldehyde to phenol of less than one and are called novolacs. Owing to the molar ratio of formaldehyde to phenol, they will not completely polymerize without the addition of a crosslinking agent. Novolacs are commonly used as photoresists. See also photolithography.
Common cross-linker used for this resin is paraformaldehyde.
Base catalysed phenol formaldehyde resins are made with a formaldehyde to phenol ratio of greater than one (usually around 1.5). Phenol, formaldehyde, water and catalyst are mixed in the desired amount, depending on the resin to be formed, and are then heated. The first part of the reaction, at around 70 °C, forms hydroxymethyl phenols. This results in a thick reddish-brown goo, the resin.
The rate of the base catalysed reaction initially increases with pH, and reaches a maximum at approx. pH = 10. The reactive species is the phenolic anion formed by deprotonation of phenol. The negative charge is delocalised over the aromatic ring, activating sites 2, 4 and 6, which then react with the formaldehyde.
Formaldehyde in solution does not exist as the aldhehyde, but instead a dynamic equilibrium is formed creating a range of methylene glycol oligomers, and the concentration of the reactive form of formaldehyde depends on the exact conditions (temperature, pH) under which the reaction occurs. Thus the reaction rate law describing phenol and formaldehyde is not a simple one, and the chemical kinetics are highly complex.
Hydroxymethyl phenols will crosslink on heating to around 120 °C to form methylene and methyl ether bridges. At this point the resin is starting to crosslink, to form the highly extended 3-dimensional web of covalent bonds which is typical of polymerised phenolic resins. It is this highly crosslinked nature of phenolics which gives them their hardness and their good thermal stability and which makes them impervious to most chemical attack and solvation. It is also the reason they are called thermosets.
Phenol can react with formaldehyde at any one of three possible sites, and formaldehyde can react with up to two phenols. Thus the theoretical functionality of phenol is three and the theoretical functionality of formaldehyde is two. The actual functionality that is found in the polymer depends on the phenol:formaldehyde ratio.
By adding a small amount of acid catalyst to phenol (something miscible, such as p-toluenesulfonic acid) and slowly adding formaldehyde, the formaldehyde will react between two phenols to form a methylene bridge, creating a dimer. This dimer is the substance bisphenol F, which is itself an important monomer in the production of epoxy resins. At higher concentrations of these dimers, there is the possibility of generating trimers, tetramers and higher oligomers. This is what occurs during the formation of bakelite. The average molecule generated depends on the ratio of formaldehyde to phenol. In bakelite this is usually around 0.8, and so, with 5 phenols for every 4 formaldehydes the average molecule is a pentamer (with respect to phenol).
When the molar ratio of formaldehyde:phenol reaches one, in theory every phenol is linked together via methylene bridges, generating one single molecule, and the system is entirely crosslinked. This is why bakelites (F:P <1) don't harden without the addition of a crosslinking agent, and why resins with the formula F:P >1 will.
WIPO ASSIGNS PATENT FOR "PROCESS FOR OBTAINING A PHENOL-FORMALDEHYDE RESIN WITH LOW FORMALDEHYDE CONTENT AND RESIN OBTAINED BY THIS PROCESS" (, ROMANIAN INVENTORS)
Jan 17, 2011; GENEVA, Jan. 17 -- Publication No. WO/2011/005132 was published on Jan. 13. Title of the invention: "PROCESS FOR OBTAINING A...
Patent No. 7,741,406 Issued on June 22, Assigned to Georgia-Pacific Chemicals for Phenol-Formaldehyde Resin (Georgia Inventors)
Jun 23, 2010; ALEXANDRIA, Va., June 26 -- James Knight and Paul Baxter, both of Conyers, Ga., Kim Tutin of East Point, Ga., and Ramji...
WIPO ASSIGNS PATENT TO GEORGIA-PACIFIC CHEMICALS FOR "METHOD OF SPRAY DRYING PHENOL-FORMALDEHYDE RESIN" (AMERICAN INVENTORS)
Jun 20, 2011; GENEVA, June 20 -- Publication No. WO/2011/072092 was published on June 16. Title of the invention: "METHOD OF SPRAY DRYING...
WIPO ASSIGNS PATENT TO GEORGIA-PACIFIC CHEMICALS FOR "BONDING WOOD COMPOSITES WITH RESIN SOLIDS-FORTIFIED PHENOL-FORMALDEHYDE RESIN" (AMERICAN INVENTORS)
Oct 31, 2011; GENEVA, Oct. 31 -- Publication No. WO/2011/133414 was published on Oct. 27. Title of the invention: "BONDING WOOD COMPOSITES WITH...
US Patent Issued to Georgia-Pacific Chemicals on Aug. 28 for "Bonding Wood Composites with Resin Solids-Fortified Phenol-Formaldehyde Resin" (Georgia, South Carolina, Alabama Inventors)
Aug 29, 2012; ALEXANDRIA, Va., Aug. 29 -- United States Patent no. 8,252,427, issued on Aug. 28, was assigned to Georgia-Pacific Chemicals LLC...